Inconel X‑750 Plates (UNS N07750) are precipitation‑hardening nickel‑chromium–iron alloys specifically formulated to deliver outstanding mechanical strength, oxidation resistance, and stress‑rupture performance in temperatures up to 700 °C. By solution‑annealing at ~980 °C followed by a two‑step aging cycle (565 °C × 16 h + 704 °C × 4 h), a uniform dispersion of γ′ precipitates (Ni₃(Al,Ti)) is achieved. This microstructure elevates yield strength above 830 MPa and tensile strength beyond 1 030 MPa, while maintaining elongation ≥ 15 % and fracture toughness.
The balanced alloying of 70–75 % Ni, 14–17 % Cr, plus Ti, Al, and minor Zr and B, gives X‑750 Plates exceptional resistance to chloride stress‑corrosion cracking, pitting, and oxidation in both oxidizing and mildly reducing atmospheres. Their weldability by TIG/GTAW or electron‑beam—followed by post‑weld aging—allows fabrication of large panels or complex assemblies without sacrificing performance. Standard plate sizes range from 2 mm to 50 mm thickness, widths up to 2 m, and lengths to customer specification, with mill‑annealed, pickled, or electropolished finishes. Custom heat‑treat cycles are available to optimize creep‑rupture life, fatigue strength, or corrosion resistance for markets in South Asia, Southeast Asia, the Middle East, Europe, and the Americas.
| Element | Content (%) |
|---|---|
| Nickel (Ni) | 70.0 – 75.0 |
| Chromium (Cr) | 14.0 – 17.0 |
| Iron (Fe) | Balance |
| Titanium (Ti) | 0.75 – 1.50 |
| Aluminum (Al) | 0.15 – 0.75 |
| Cobalt (Co) | ≤ 1.00 |
| Manganese (Mn) | ≤ 1.00 |
| Silicon (Si) | ≤ 1.00 |
| Carbon (C) | ≤ 0.08 |
| Sulfur (S) | ≤ 0.015 |
| Phosphorus (P) | ≤ 0.015 |
| Copper (Cu) | ≤ 0.50 |
| Boron (B) | 0.003 – 0.010 |
| Zirconium (Zr) | ≤ 0.02 |
| Condition | Yield Strength (MPa) | Tensile Strength (MPa) | Elongation (%) | Hardness (HRC) |
|---|---|---|---|---|
| Mill‑Annealed (∼980 °C) | ~345 | ~760 | ≥ 40 | ≤ 90 HRB |
| Aged (565 °C × 16 h + 704 °C × 4 h) | ≥ 830 | ≥ 1 030 | ≥ 15 | 35 – 45 |
| Property | Value |
|---|---|
| Density | 8.21 g/cm³ |
| Melting Range | 1260 – 1340 °C |
| Thermal Conductivity (20 – 600 °C) | 11 W/m·K |
| Specific Heat Capacity (25 °C) | 439 J/kg·K |
| Coefficient of Thermal Expansion (20 – 100 °C) | 13.4 µm/m·°C |
| Electrical Resistivity (20 °C) | 1.0 µΩ·m |
| Magnetic Permeability | ≈ 1.002 (non‑mag.) |
ASTM B637 / SB‑637 – Precipitation‑hardened nickel‑alloy plate
AMS 5664 – Special quality Inconel X‑750 plate
ASME SB‑637 – Boiler & Pressure Vessel Code
Inconel X‑750 Plates are employed in:
Aerospace – Turbine shrouds, combustor liners, hot‑section panels
Power Generation – Superheater/reheater panels, boiler tubesheets
Chemical Processing – Heat‑exchanger plates, reactor liners, flare stacks
Nuclear – Steam‑generator tubing support plates, spacer grids
Oil & Gas – Downhole packer plates, subsea control‑module panels
Marine – Desalination plant coils, seawater cooling panels
Q1: What distinguishes X‑750 Plates in high‑temperature service?
The γ′ precipitate microstructure imparts superior creep‑rupture
resistance and fatigue life up to 700 °C, while chromium content
ensures oxidation protection.
Q2: Can X‑750 Plates be welded without loss of properties?
Yes—TIG/GTAW and electron‑beam welding are standard; a post‑weld
aging treatment fully restores precipitation‑hardening and
mechanical strength.
Q3: Are custom thicknesses and finishes available?
Absolutely. Standard thicknesses span 2–50 mm, widths up to 2 m;
finishes include mill‑annealed, pickled, and electropolished.
Custom heat‑treat cycles can optimize specific properties.
|
|